Abstract
The goal of this work was to investigate formability of AZ31B magnesium alloy during incremental equal channel angular pressing (I-ECAP). Square billets were processed using different routes of I-ECAP at temperatures varying from 125 °C to 250 °C. The billets were obtained from commercially available coarse-grained, hot-extruded rod and fine-grained, hot-rolled plate. A strong influence of the initial microstructure on processing temperature was reported. Fine-grained samples were successfully processed at 200 °C, while coarse-grained ones must have been heated up to 250 °C to avoid fracture. A gradual temperature decrease with subsequent passes allowed successful pressing at 150 °C. Processing using various routes of I-ECAP showed that a billet rotation before the last pass had strong influence on mechanical properties. The results of experiments were plotted on the diagram of allowable processing temperature for AZ31B. It was found that the relation between the minimum temperature in I-ECAP and the initial grain size could be described by a logarithmic equation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.