The Effect of Hydrogen on the Kinetics of Solid Phase Epitaxy in Amorphous Silicon

Abstract

AbstractThis paper discusses the intrusion of H into a-Si layers during solid phase epitaxy and the effect of this H on the growth kinetics. We show that during annealing in the presence of water vapor, H is continuously generated at the oxidizing a-Si surface and diffuses into the amorphous layer, where it causes a reduction in the epitaxial growth rate. The measured variation of growth rate with the depth of the amorphous/crystal interface is correlated with the concentration of H at the interface. The diffusion coefficient for H in a-Si is determined by comparing measured depth profiles with calculated values. Hydrogen intrusion is observed even in layers annealed in vacuum and in inert gas ambients. Thin (<;5000 Åthick) a-Si layers are especially susceptible to this effect, but we show that in spite of the presence of H the activation energy for SPE derived earlier from thin-layer data is in good agreement with the intrinsic value obtained from thick, hydrogen-free layers.