Abstract
The purpose of the present study was to evaluate the effects of human blood on the setting and microhardness of calcium silicate cements. Three types of silicate-based cements were used: ProRoot MTA (PMTA), OrthoMTA (OMTA), and RetroMTA (RMTA). Mixed cement was placed into polyethylene molds with lengths of 2 and 4mm. After storage for 4days under three different storage conditions, i.e., saline, saline after 5min of human blood, and human blood, the polyethylene molds were removed. With the specimens set, the surface microhardness was measured using a Vickers microhardness tester, crystalline structure was analyzed with X-ray diffraction (XRD), and the surface characteristics were examined with scanning electron microscopy (SEM). All specimens of 4mm in length were set with all materials, and the blood groups exhibited lower microhardnesses than did the saline groups (p<0.05). Among the 2-mm specimens that were stored in blood, the numbers of specimens that set were significantly different across the materials (p<0.001). Regarding the microhardnesses of the RMTA and OMTA groups, there were no significant differences between storage conditions. For the PMTA group, only one specimen that was set in the blood group exhibited reduced microhardness. XRD showed changes of crystalline structure in the PMTA and OMTA blood group, whereas RMTA did not. SEM analysis revealed more rounded and homogeneous structures and demonstrated a clear lack of acicular or needle-like crystals in the PMTA and OMTA blood groups, while RMTA did not reveal substantial differences between the saline- and blood-stored groups. Blood contamination detrimentally affected the surface microhardnesses of all materials; furthermore, among the 2-mm specimens, blood contamination interfered with normal setting. Therefore, RMTA might be a more suitable choice when blood contamination is unavoidable due to limited depth. Clinical relevance RetroMTA might be a more suitable choice in situations in which blood contamination is unavoidable.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.