Abstract
In this study, Ti-6Al-4V bars were first prepared by extrusion of powder compacts from blended powder mixtures in the beta phase region, then the as-extruded bars were heat-treated following four different conditions: beta quenching and aging (βQA), broken up structure (BUS) treatment, solution treatment and aging (STA) and recrystallization annealing (RA). The effect of the heat treatments on microstructure and mechanical properties was studied using optical microscopy, scanning electron microscopy, and mechanical test to determine which heat-treatment condition has the greatest impact on the mechanical properties of the as-extruded Ti-6Al-4V alloy. The results show that the as-extruded condition has the best balance of strength (1120 MPa of UTS) and ductility (11% of elongation to failure). βQA and STA lead to a slight increase in strength but ductility decreases considerably. After BUS and RA treatments, both strength and ductility are reduced. The relationship between processing, microstructure and properties was studied, and their implications towards fatigue behaviour and fracture toughness were discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.