Abstract

It was shown in Ni53Mn25Ga22 single crystals that the annealing at 1273 K for 1 h followed by slow cooling, at which the (L21+γ)-structure is formed, provides the increase of crystals plasticity as compared with the brittle initial L21-single crystals. The increase of critical stresses by more than 2 times (up to σ > 150 MPa), at which the cooling/heating cycles under stress are accompanied by sample destruction, is observed. Moreover, the value of thermal hysteresis is increased by 1.5 times and the perfect curve of superelasticity is observed at T=423 K.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.