Abstract
mpact of heat treatment on durability has been evaluated in this study in conditions of high-temperature creep of castings made from nickel superalloy MAR-247 post production rejects. Castings made in the processes of modification and filtration when pouring into moulds were subject to solubilization (1185°C/2 h) with subsequent ageing (870°C/20 h). It has been found on the basis of performed tests that in conditions of high-temperature creep at temperature 980°C with stress σ = 150 MPa the resistance of specimens of coarse-grain structure was significantly higher when compared to fine-grain material. The conditions of initiation and propagation of cracks in these specimens were analysed with consideration of morphological properties of material macro-, micro-and substructure. Moreover, it has been proven that creep resistance of heat treated MAR-247 superalloy significantly improves when compared to its condition after the process of modification only. Macrostructural changes in the MAR-247 superalloy that determine the increase of superalloy creep resistance after solubilization and ageing, as observed in the tests, were also examined.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.