Abstract
AbstractSurface initiated rolling contact fatigue (RCF) of gears and rolling bearings can lead to premature failure in mechanical transmission systems. The orientation of surface crack initiation closely depends on surface tractive force, while the mechanism leading to this dependence is still obscure. In this work, a numerical model is proposed to investigate the effect of friction on surface crack initiation in RCF. An inhomogeneous contact solver based on semi‐analytical method (SAM) is developed by combining the damaged‐coupled constitutive relation and the Eshelby's equivalent inclusion method. The damage accumulation and concurrent degradation of material properties are modeled with continuum damage mechanics (CDM). The effect of surface tractive force on the orientation of surface crack initiation is simulated and analyzed. Results indicate that the progressive evolution of damage under the cyclic loading is accompanied by the stress variation around the damaged area. The damaged area increases, and the crack initiation life decreases with an increasing coefficient of friction.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Fatigue & Fracture of Engineering Materials & Structures
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.