Abstract
Three kinds of colloidal silica (GS-30, AM and HS-30) were applied as binders to corundum-mullite castables. The apparent porosity and cold modulus of rupture for samples fired at 800 oC and 1000 oC were compared. The fractography of colloidal silica bonded corundum-mullite castables was carried out by slit island method. The microstructure of fracture surface was characterized by scanning electron microscope. The results showed that castables by using imported colloidal silica (AM and HS-30) presented higher strength than those with domestic (GS-30), which was determined by the activity of silica and modified ion. The difference of the size distribution of the salient on the fracture surfaces indicated that the strength of castables was dependent on the bonding among the components.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.