Abstract
In this study, the effect of deposition temperature of TiN thin films deposited using the thermal atomic layer deposition (ALD) method was investigated. TiCl4 precursor and NH3 reactive gas were used, and the deposition rate, resistivity change, and surface morphology characteristics were compared in the deposition temperature range of 400 °C–600 °C. While resistivity decreased to 177 µΩcm as the deposition temperature increased to 600 °C, an increase in surface roughness (Rq) to 0.69 nm and a deterioration in the step coverage were identified. In order to obtain a high-quality TiN thin film with excellent resistivity and step coverage characteristics even at low deposition temperatures, the TiN thin film was post-treated with plasma in a combination of N2/He gas ratio of 3:2 to confirm the change in resistivity. X-ray diffraction analysis confirmed crystallization change in the TiN thin film caused by plasma energy. As a result, the resistivity of the TiN thin film deposited at 400 °C was confirmed to be lowered by about 25%.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.