Abstract
Non-oriented 3% silicon steel sheets were cold-rolled to 0.1 mm thick by various methods, and then they were finally annealed in an argon atmosphere for 1.5 hours at 900/spl deg/C with a cooling rate of 0.025/spl deg/C/s. Their magnetic properties changed depending on cold-rolling method used. A sample which had magnetic two-easy-directions with strong [100] cubic texture was obtained in the following way. The sample was alternately cold-rolled in two perpendicular directions L and T, and was also subjected to an intermediate anneal. The average grain diameter of the sample was 57 /spl mu/m. Its magnetic induction at 800 A/m was 1.65 T in the L direction, and 1.62 T in T direction, respectively.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.