Abstract
The effect of Co substitution on the crystal structure and electrical transport properties of La0.85Ag0.15Mn1−yCoyO3 compounds (0≥y≤0.50) has been studied. Structural transition from rhombohedral to orthorhombic symmetry has been observed with Co doping. The lattice parameters are found to increase with doping up to y=0.20, then it decreases. It is explained on the basis of transition from high spin state to low spin state of Co ions with increase in doping beyond y=0.20. Ferromagnetic (FM) metallic behavior with colossal magneto-resistivity has been observed up to y=0.10. However, for y≥0.15 compounds, the temperature dependence of resistivity ρ(T) follows semiconducting behavior. The electrical resistivity in the metallic region could be explained based on electron–electron and electron–magnon scattering mechanisms. The data in the semiconducting region could be explained based on the variable range hopping model for y=0.2 and adiabatic small polaron hopping model for y≥0.3.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.