Abstract
The effect of digested sewage sludge as a fuel additive to reduce corrosion of furnace walls has been studied. The nickel base alloy Alloy 625 and the iron–chromium–aluminium alloy Kanthal APMT™ were exposed for 14.25h at the furnace wall in a power boiler burning 100% used (also known as waste or recycled) wood. The test was then repeated with the addition of sewage sludge to the waste wood. The samples were chemically analysed and thermodynamically modelled and the corrosion mechanisms were investigated. The results showed that the co-firing of sewage sludge with recycled wood leads to a reduction in the corrosion. Attack by a potassium–lead combination appeared to be the main corrosion mechanism in Alloy 625 during waste wood combustion, while attack by alkali chloride was found to be dominant in APMT alloy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.