The effect of CNTs/PEEK coating thickness on the friction and wear behavior of porous Ti‐30Ta alloys for biomaterial implants

Abstract

AbstractElectrophoretic deposition was used to deposit carbon nanotube/polyether ether ketone (CNTs/PEEK) composite coatings onto porous titanium‐tantalum (Ti‐30Ta) substrates at different PEEK concentrations (4.5, 6.0, and 7.5 mg/mL). Coatings were analyzed for thickness, porosity, surface roughness, microhardness and bonding strength, with higher PEEK concentrations producing thicker and more uniform coatings. However, optimal coating thickness showed highest bonding strength; lower and higher thickness led to decreased bonding strength. The tribological properties of the CNTs/PEEK coated Ti‐30Ta samples of different thicknesses (50, 70, and 100 μm) were evaluated using ball‐on‐flat linear reciprocating sliding tests under dry and wet conditions using simulated body fluid (SBF) as a lubricant. The CNTs/PEEK coatings provided excellent tribological protection under dry friction, with thicker coatings having lower friction and negligible wear. However, under wet sliding, the coating's wear rate increased significantly due to softening of the rubbing surface caused by SBF lubrication that increase transfer film onto the counter body surface. Coating with optimal thickness of 74 μm demonstrated the lowest friction and wear under SBF lubrication due to its highest hardness and bonding strength. This study highlights the importance of controlling coating thickness in determining the performance of the CNTs/PEEK coatings for orthopedic implants.