Abstract
The effect of a 10 nm Ce coating layer on long term oxidation behaviour (up to 3000 hours) of a Fe–22%Cr ferritic stainless steel for solid oxide fuel cell (SOFC) interconnect application is investigated. Scanning transmission electron microscopy (STEM) and electron energy loss spectroscopy (EELS) analysis showed segregation of Ce to the grain boundaries of Cr,Mn spinel layer adjacent to the scale-gas interface. The findings in this study are in line with the grain boundary blocking model for the Ce effect mechanism. However, segregation of Ce was observed at the grain boundaries of the (Cr,Mn) spinel in the vicinity of the scale-gas interface. No evidence of Ce segregation was found in the grain boundaries of the chromia layer, neither any Ce rich particle was observed in the chromia layer after longer exposure times.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.