Abstract
In this study, Al 2O 3 and Al 2O 3–13 wt% TiO 2 were plasma sprayed onto AISI 316L stainless-steel substrate with and without Ni–5 wt% Al as bond coat layer. The coated specimens were characterized by optical microscopy, metallography and X-ray diffraction (XRD). Bonding strength of coatings were evaluated in accordance with the ASTM C-633 method. It was observed that the dominant phase was Al 2O 3 for both coatings. It was also found that the hardness of coating with bond coat was higher than that of coating without bond coat. Metallographic studies revealed that coating with bond coating has three different regions, which are the ceramic layer (Al 2O 3 or Al 2O 3–13 wt% TiO 2), the bond coating, and matrix, which is not affected by coating. The coating performed by plasma-spray process without bond coating has two zones, the gray one indicating the ceramic layer and the white one characterizing the matrix. No delamination or spalling was observed in coatings. However, there are some pinholes in coating layer, but they are very rare. The bonding strength of coatings with bond coat was higher than that of coating without bond coat. The strength of adhesion and cohesion was determined by means of a planemeter. It was seen that percentage of cohesion strength was higher than that of adhesion strength.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.