Abstract
The effect of maleated polypropylene (MAPP) as binder on the mechanical properties of kenaf fibre/polypropylene (KF/PP) composites is studied. Ratios between kenaf fibre and PP having 10:90, 30:70 and 50:50 in weight ratio were selected. Further, MAPP having 1, 3 and 5 percent in percentage of weight ratio was mixed in KF/PP composites. Hot press machine was used to produce tensile test samples of KF/PP composites. The mechanical properties that are tensile strength, tensile modulus and elongation at break of KF-PP composites were obtained from tensile test result. It is found that the tensile strength and tensile modulus increase with increasing the kenaf fibre loading and higher percentage of MAPP. Further, the elongation at break for KF/PP composites shows lower result when increasing of kenaf fibre loading. However, when percentage of MAPP added in KF/PP composites increases, the elongation at break increased slightly. Thus, result shows that kenaf fibre/PP composites with binder were better in tensile strength, tensile modulus however the elongation at break shows weak result unless the binder was added.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.