Abstract
This study examined the fatigue life (Nf) and fatigue limit (FL) of AISI 4340 steel in relation to surface roughness, artificial defects and shot peening. Artificial surface defects on fatigue specimens were obtained by electrical discharge machining (EDM) or by pre-corrosion in 3.5% NaCl and perchloric acid solutions, followed by a fatigue test. The presence of artificial defects of various sizes, taken into account by the area parameter, led to a significant decrease in fatigue characteristics, while shot peening contributed to their noticeable improvement. Defects resulting from electrochemical corrosion had a much greater negative effect on fatigue life than defects introduced by EDM.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.