Abstract
Microalloying with Nb and B leads to a granular bainite microstructure which is composed of a bainitic ferrite matrix and a uniformly distributed martensite/austenite-constituent in the as-rolled condition. Due to this transformation strengthening mechanism, high strength and toughness could be achieved even though the C content was extremely low. It was found that both dissolved Nb in austenite and free B are prerequisites for granular bainite formation. Furthermore, there is a critical B content to achieve the complete bainitic transformation strengthening effect. The critical B content increases with C content. C thus diminishes the effect of B in promoting bainite transformation, due to the formation of boron carbides or the depletion of dissolved Nb in austenite. The effect of Mn, Mo and Ni on the decomposition of austenite is similar. A parameter“Mneq” which relates the effect of these alloying elements on the Bs temperature was derived. It was confirmed that the strength of bainitic steels is inversely proportional to theBs temperature.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.