Abstract
Lightweight impermeable ceramic bodies were designed by combining pore templating and controlled viscous sintering through in-situ crystallization. Various amounts of limestone were added to a glass-fluxed low-temperature stoneware tile formulation. Closed porosity was created by decomposition of carbonates prior to sintering, thus leaving voids that were not completely filled by the viscous melt. The resulting oxides chemically modified the liquid phase and promoted the crystallization of β-wollastonite, diopside and anorthite. Hence, viscous sintering was affected. The addition of limestone brought on several advantages: the temperature of maximum sintering rate was decreased (<900 °C); the dimensional stability range was extended; the matrix was reinforced by newly-formed crystals that compensated for the global structure weakening evoked by increased porosity; an increase in whiteness was observed in concomitance to crystallization, reaching values only obtained when using zircon as opacifier (L*=87).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.