Abstract
Abstract The effect of ageing on the tensile behaviour, mode I fracture toughness and mixed mode I/III fracture toughness of 7010 aluminium alloy plate was investigated. It was found that the 0.2% proof stress in this alloy increased from the under-aged temper to the peak-aged (T6) temper and then subsequently decreased in the over-aged (T73) temper. On the other hand, the ductility exhibited a monotonic decrease from the under-aged temper to the over-aged temper. The Ludwigson equation was found to best describe the flow behaviour in all the three ageing tempers. Under mode I as well as mixed mode I/III loading, the highest fracture toughness was seen in the under-aged temper, whereas the fracture toughness values in the peak-aged and over-aged tempers were comparable.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.