The early wear susceptibility of cementum, enamel and dentine in vitro

Abstract

ObjectivesTo assess the differential early wear susceptibility of cementum, enamel and dentine at a micron level. MethodsWhole human molar buccal surfaces incorporating natural enamel and cementum (n = 20) confirmed by imaging (digital microscopy: Keyence, VHX-7000 Milton Keynes, UK), were mounted, scanned (profilometry: XYRIS 4000, Taicaan, Southampton, UK), and allocated to receive erosion (citric acid, pH 2.7, 30 min (n = 10)) or erosion/abrasion challenges (3 cycles of (citric acid, pH 2.7, 10 min, 60 300 g linear abrasion strokes), n=10). Samples were polished and the experiment repeated on polished enamel, and polished coronal and radicular dentine within the same tooth. Profilometric wear data were obtained using superimposition: GeoMagic (3Dsystems, Darmstadt, Germany) and subtraction: MountainsMap (DigitalSurf, Besancon, France). Data were normal. A general linear model was used to assess differences between groups and substrates. ResultsThe mean step height (SD) for natural enamel was 8.82 μm (2.53) for erosion and 11.48 μm (2.95) for erosion/abrasion. For natural cementum, the mean step height was 6.00 μm (2.29) for erosion and 4.67 μm (1.58) for erosion/abrasion. Dentine step heights ranged from 7.20 μm (1.53) for erosion and 9.79 μm (1.01) for erosion/abrasion with no statistical differences in dentine wear. Natural cementum surfaces had the lowest wear (p<0.001). Dentine had significantly less wear than natural enamel (p<0.02). ConclusionsCementum surfaces demonstrated the most wear resistance, followed by dentine under erosion dominant conditions in this in vitro study. Further in-vivo investigations are needed to confirm the intraoral stability of cementum. Clinical SignificanceCementum may be the least susceptible of dental substrates to wear and dentine does not wear at a faster rate than enamel under erosive conditions. This adds to our knowledge on the development of non-carious cervical lesions and questions whether wear rates will accelerate once dentine is exposed.