Abstract
In recent years great attention has been placed by the building sector on alkali-activated technology based on metakaolin, fly ash and ground granulated blast furnace slag (GGBFS), but also on emerging precursors such as by-products from non-ferrous metallurgy. The present work focuses on the development of alkali-activated binders from two slags, one from primary and one from secondary copper production, which were finely milled, blended with GGBFS, and activated with K-based alkali silicate solution with a 1.7 SiO2/K2O molar ratio. The aggregate to paste mass ratio was 2. The mixtures were cast, and cured for a designated time at room temperature and 60% RH. The so-obtained paving blocks were then tested in accordance with European standard for concrete paving blocks. The following properties were measured: splitting tensile strength, abrasion resistance, slip and skid resistance, resistance to freeze-thaw and resistance to freeze-thaw in the presence of de-icing salts. Their properties were compared to those of commercially available concrete paving blocks, and it was found that the performance of the alkali-activated pavers was generally comparable with the concrete pavers, while certain properties (e.g., abrasion resistance, freeze-thaw resistance and freeze-thaw resistance in presence of de-icing salts) were considerably better.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have