Abstract
The crystallization of fluoroapatite is of importance because a number of biological systems makes use of this mineral in teeth (sharks) or for protection (molluscs). The crystallization of fluoroapatite was performed on titanium metal, on polymer (poly(ethylene-co-1,4-cyclohexane-dimethylene-terephthalate), PETG), and in a tubular reactor made of polytetrafluoroethylene (PTFE). A special morphogenesis leading to a distinct dumbbell-like morphology was observed. The morphology was clearly dependent on the external parameters pH and supersaturation. Secondary parameters were the crystallization time, the ionic strength, and the stoichiometric ratios of calcium, phosphate, and fluoride. Dumbbells were only observed in the pH range of 5−7. Two different growth mechanisms for fluoroapatite at a pH of 5−6 and a pH of 6−7 are proposed, based on branching hexagonal prisms and on branching spikes, respectively. The presence of charged additives (cationic and anionic surfactants, poly(aspartic acid), polylysine) led to inhibition of the crystal growth, suggesting an electrostatic blocking of the crystal growth sites. An increase in the ionic strength did not influence the crystal morphogenesis.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.