Abstract
The poly(lactic acid) (PLA)/montmorillonite (MMT) composites were prepared by melt blending in an internal mixer. The effect of MMT and organically modified MMT (OMMT) addition on crystallization and mechanical preferences has been studied. The DSC results show that the crystallization ability of PLA is improved by MMT or OMMT. The addition of MMT and OMMT increase the crystallinity of PLA from 27.3 to 32.8%, and the cold crystallization temperature (TCC) of PLA decreases from 93.1 to 88.9°C with the MMT. However, the nucleating effect of MMT is better than that of OMMT due to the velvety surface resulted from the organic modification. The average size of the spherulites in PLA/MMT is smaller than that in PLA/OMMT. The addition of MMT or OMMT increases the tensile strength of PLA from 29.6 to 34.7 MPa and decrease the elongation at break of PLA. The modulus of PLA composites is enhanced rapidly from 338 to 660 MPa by the addition of MMT.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.