Abstract
The influence of Fe on the nucleation potency of TiB2 particles was investigated by employing grain refinement of high purity aluminium in this study. Experiment results showed that without Fe, high purity aluminium cannot be refined by 0.8wt.% addition of Al-5Ti-1B. However, high purity aluminium containing 0.08wt.% Fe can be refined effectively by 0.2wt.% addition of Al-5Ti-1B, its grain size was about 206µm in diameter. Fine equiaxed grains of about 153µm in diameter can be obtained for high purity aluminium containing 0.08wt.% Fe and 0.006wt.% Ti. Grain refinement mechanism should include nucleation and dendrite remelting and multiplication. Both nucleation and dendrite remelting and multiplication played essential role on the grain refinement of aluminium. The effect of Fe was linked to increase active nuclei by segregation on TiB2 surface and then to promote nucleation of α-Al. The performance of Ti was to enhance the dendrite remelting and multiplication by forming small conglomeration zones of Ti atoms concentrated around TiB2 particles.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: IOP Conference Series: Materials Science and Engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.