The corrosion behavior of several heat resistant materials in air + 2 vol-% Cl2 at 300 to 800 °C. Part I - Fe-base and Fe-containing alloys

Abstract

In the present paper the corrosion behavior of 2 1 / 4 Cr1Mo steel, Alloys 800H, AC66, 45TM and 690 was investigated at 300 to 800 °C in dry air and synthetic air with 2 vol.-% Cl2. The data reveal that the major role determining corrosion resistance are played by Fe in the alloys. In particular if the same Cr-contents are present in the alloys it is only the Fe content which decides on resistance against Cl-attack while additions of even almost 3 % of Si evidently have only little effort. Das Korrosionsverhalten verschiedener hitzebestandiger Werkstoffe in Luft mit 2 % Cl2 bei Temperaturen von 300 bis 800 °C. Teil I – Fe-Basis- und Fe-haltige Legierungen In der vorliegenden Arbeit wurde das Korrosionsverhalten der Werkstoffe 10CrMo910, Alloy 800H, AC66, 45TM und 690 in trockener Luft und synthetischer Luft mit 2 % Cl2 bei Temperaturen von 300 bis 800 °C untersucht. Es zeigt sich, das die Korrosionsbestandigkeit der Werkstoffe in erster Linie durch den Fe-Gehalt der Legierungen bestimmt wird. Dies gilt insbesonders, wenn Werkstoffe mit gleichen Cr-Gehalten verglichen werden. Zusatze von fast 3 % Si schienen dagegen nur eine vergleichsweise geringe Wirkung zu besitzen.