Abstract
The pitting corrosion of the passive films formed on the surface of sputter-deposited W-30Ti and W-53Ti alloys after immersion for 24 hours in alkaline 1 M NaOH soution at 25°C was studied by using the surface sensitive technique of the confocal scanning laser microscopic (CSLM) technique including corrosion tests and electrochemical measurements. The higher corrosion rate of the W-30Ti alloy (i.e., about 3x 10-2 mm/y) than those of the W-53Ti and W-90Ti alloys (i.e., about 4-5 x 10-3 mm/y) was mostly due to the deep type of pitting corrosion observed on the surface of the passive film formed on the W-30Ti alloy in 1 M NaOH solution. The shallow type of pits was developed on the surface of the passive film formed on the W-53Ti alloy, whereas no pitting corrosion on the titanium-rich W-90Ti alloy.Keywords: Pitting corrosion; Open circuit corrosion potential; Corrosion test; CSLM studyTribhuvan University Journal Vol. XXVI, No. 1, 2009 Page: 17-26
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.