Abstract
Abstract This work explores the influence of dopant concentration on photoluminescent emission and kinetics of Eu3+-doped (0.2−10 at.%) nanocrystalline lanthanumoxide powders. The X-ray diffraction analysis confirmed that all samples crystallize in La2O3 hexagonal phase with space group P3¯ m1. Transmission electron microscopy showed particles with non-uniform shape and diverse size distribution with an average particle size of (95 ± 5) nm. The room temperature photoluminescence spectra of all samples contain characteristic Eu3+ luminescence lines with the most pronounced red 5D0 →7F2 emission at about 626 nm. The maximum intensity of red emission is observed for the sample containing 5at.% of Eu3+ ions. The emission kinetics was recorded in the temperature range from 10K to 300 K. The maximum lifetime value of 0.98 ms obtained for the sample with 0.5at.% Eu3+ at room temperature increases up to 1.3ms at 10 K.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.