Abstract
Experiments carried out on pultruded fibre reinforced polyester resins show that, at moderate fibre volume fractions, the compressive strength of aligned fibre composites depends linearly on the volume fraction. The strength falls off when the fibre volume fraction,V f=0.4 with Kevlar and high strength carbon fibres. The effective fibre strength atV f<0.4 is much less than the tensile strength but it is close to the tensile strength with E-glass fibres and high modulus carbon fibres. Poor adhesion between fibres and matrix reduces the compressive strength, as does kinking the fibres when the fibre radius of curvature is reduced to below 5 mm. Misalignment of the fibres reduces the compressive strength when the average angle of misalignment exceeds about 10° for glass and carbon fibres. However, with Kevlar no such reduction is observed because the compression strength of Kevlar reinforced resin is only a very little better than that of the unreinforced resin.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.