Abstract
In this paper, Nd:YAG ceramic was prepared by combustion synthesis with centrifugation casting. Combustion temperature and pressure were calculated under adiabatic hypothesis, and measured experimentally by W/Re thermocouple and piezometer, respectively. The combustion temperature and pressure decreased with increase of the content of diluents (Y2O3 and A12O3). The YAG could be obtained as the ratio between the Y2O3 and A12O3 reached 3:5. Phase composition and microstructures of the derived products were analyzed by XRD, SEM and EDS. The results show that the other reaction product TiN and a small quantity of gas and oxide impurity were not completely separated from YAG melt under centrifugal force so that transparent YAG ceramic was not obtained in this work.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.