Abstract
ABSTRACT This study examines the influence of density variations in coconut palm wood (Cocos nucifera L.) on bond strength development using three types of adhesives: urea formaldehyde (UF), melamine urea formaldehyde (MUF), and polyvinyl-acetate (PVAc). A special testing device called Automated Bonding Evaluation System (ABES) was used to investigate the bond strength development between coconut veneers as a function of adhesive type, wood density (moisture content of 10%), pressing time, and bond-temperature development. Coconut wood density was shown to greatly affect the bond line. The bond strength of medium-density material (600–700 kg/m3) was lower than that of high-density material (900–1,000 kg/m3). Interestingly, the medium-density coconut veneers achieved higher bond strength with shorter pressing times, while the high-density coconut veneers reached better results with longer pressing times. Moreover, the bond strength improved by increasing the hot-pressing time resulting in higher bond-line temperatures. A comparison was made between coconut wood and beech wood for similar bonding parameters.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.