Abstract
The p-type InP:Zn was prepared by the liquid encapsulated Czochralski method and subsequently implanted with Mn + of 5 × 10 15 cm −2. The results of energy dispersive X-ray displayed that the concentration of incorporated Mn into InP:Zn is 1 at.%. The cross-sectional transmission electron microscopy showed that the thickness of Mn-incorporated layer was ∼300 nm. For photoluminescence measurements, the Mn-related optical transitions caused by incorporation of Mn were broadly observed at the energy region of 1.034, 0.985, and 0.958 eV. The samples clearly showed ferromagnetic hysteresis loops at 10 K, and the ferromagnetic behavior was observed to persist up to 360 K. Thus, the Curie temperature of Mn +-implanted InMnP:Zn (Mn ∼ 1 at.%) is expected to be above 300 K. It is found that a room-temperature-ferromagnetism of InMnP:Zn can be formed by ion implantation of a relatively low concentration of Mn (1 at.%).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.