Abstract
Abstract One of the most inexpensive and effective method to protect steel against corrosion is paints containing active pigments. The traditional way to test these coatings performance is by accelerated tests (exposition to salt spray and/or humidity chambers) and electrochemical tests (corrosion potential, ionic resistance and electrochemical impedance spectroscopy). However, these tests give incomplete information if the results are not correlated to outdoor or service tests. The aim of this work was to evaluate water-borne epoxy anticorrosion paints containing different commercial phosphate pigments. The paints were exposed to a semi-industrial atmosphere for 7 years. Electrochemical tests and accelerated assays were also done in order to find a correlation between laboratory and service tests. The results obtained showed no correlation between those from pigment suspensions and those from painted panels, as it seemed that paint performance is highly dependent on the resin. The pigments zinc iron phosphate and zinc aluminium phosphate performed poorly in pigment suspensions. However, the coatings containing them exhibited the highest ionic resistance, the lowest film capacitance and gave the better results in outdoor tests. Results in outdoor exposure tests correlated with those from impedance measurements.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.