TFA-MOD법을 이용한 YBCO 박막의 열처리 온도와 두께의 영향

Abstract

We fabricated the YBCO films on LAO substrate using the TFA-MOD method and evaluated the effects of heat treatment temperature and film thickness on the microstructure, degree of texture, and critical properties. The calcining and firing were peformed at the temperature range of , respectively. For the films fired at after calcining at showed highest critical temperature (Tc-onset) of 89.5 K and critical current (Ic) of 40A/cm-width which corresponds to critical current density (Jc) of . The highest critical properties are probably attributed to the formation of purer YBCO phase, stronger biaxial texture, and higher oxygen content, according to the XRD, pole-figure, SEM, Raman analysis. From the multi-coated films, the Ic increased from 39 to 169 A/cm-width as the coating repeated to four times, while the corresponding Jc was measured from once to be in the range of . Both Ic and Jc degraded as the coating repeated further, indicating that the optimum thickness is in the range of .