Abstract
Texture evolution during static primary recrystallization of an austenitic Fe-28Mn-0.28C TWIP steel was analyzed. The cold-rolled material, which showed a Brass-type texture at medium (30% and 50%), and additionally a γ-fiber at high (80%) deformation degrees, was subjected to isothermal annealing at 700°C. The influence of rolling degree/starting texture on the development of particular texture components was studied. After recrystallization a weakened, retained rolling texture was observed for the examined reduction levels. In addition to the deformation components, Brass and Goss, further α-fiber components were formed mainly by annealing twinning leading to the development of this fiber.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.