Abstract
The studies were carried out on three Ni-Mn-Ga polycrystalline alloys with the 10M martensite and the L21 parent phase. The specimens were cut along the [001] and [110] directions of the columnar grains from the ingots of either round or flat shape. The samples were heated up to 10000C and rolled in one direction in several steps. The final reduction of the samples thickness was: 28%, 36%, 57% and 69%. The texture of the initial [001] orientation rolled with the highest deformation 60% shows the following orientation components: {111}<112>, {112}<011>, {111}<011> which are typical for deformed and recrystallized metals of the A2 structure. The texture of the specimen with the initial [110] orientation rolled with 69% can be described as a fibre texture scattered around the <110> direction.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.