Abstract
Protection of Ceramic Matrix Composites (CMCs) is rather an important element for the engine manufacturers and aerospace companies to help improve the durability of their hot engine components. The CMC’s are typically porous materials which permits some desirable infiltration that lead to strength enhancements. However, they experience various durability issues such as degradation due to coating oxidation. These concerns are being addressed by introducing a high temperature protective system, Environmental Barrier Coating (EBC) that can operate at temperature applications<sup>1, 3</sup> In this paper, linear elastic progressive failure analyses are performed to evaluate conditions that would cause crack initiation in the EBC. The analysis is to determine the overall failure sequence under tensile loading conditions on different layers of material including the EBC and CMC in an attempt to develop a life/failure model. A 3D finite element model of a dogbone specimen is constructed for the analyses. Damage initiation, propagation and final failure is captured using a progressive failure model considering tensile loading conditions at room temperature. It is expected that this study will establish a process for using a computational approach, validated at a specimen level, to predict reliably in the future component level performance without resorting to extensive testing.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call