Tension/compression asymmetry in creep behavior of a Ni-based superalloy

Abstract

The effect of temperature on the tensile behavior and deformation mechanisms in a single crystal superalloys CMSX-4 is addressed and deduced by transmission electron microscopy in the temperature range from room temperature to 1100 °C. It is found that the tensile yield strength reaches a peak at 800 °C. And then, the yield strength decreases with increasing temperature. At room temperature, anti-phase boundary shearing dominates the plastic deformation. From 800 °C to 850 °C, the plastic deformation mechanism is mainly controlled by stacking fault shearing. The Kear-Wilsdorf locks have also appeared. When the temperature reaches at 950 °C, dislocation loops with anti-phase boundary shearing of the γ′precipitates are presented. Above 950 °C, the plastic deformation mechanism is processed by the rafted structure of the γ′precipitates by-passing, i.e., Orowan by-passing and dislocation climb. Finally, according to the experimental results, the variety of stacking faults with temperatures and the relationship between the yield strength and plastic deformation mechanism are discussed.