Abstract

Homogeneous low voltage electron beam irradiation (HLEBI) with small dose of 0.30 to 1.17 MGy enhanced the elasticity indicated by the initial and maximum slope values of stress–strain curves ((dσ/dε)i and (dσ/dε)max) of 250 µm diameter optical fiber (OF), which was constructed with both core (10 µm diameter) and clad (125 µm diameter) silica glasses covered with acryl-urethane sheath (62.5 µm thickness). The highest (dσ/dε)i and (dσ/dε)max values of 5.3 and 5.9 GPa, which were about 10 and 20% higher than those (4.8 and 4.9 GPa) before irradiation, were found at 0.104 MGy, respectively. Moreover, remarkable effects of HLEBI of 0.65 MGy on both tensile strength (σf) and fracture strain (εf) of OF were obtained at each fracture probability (Pf) value. Since HLEBI also enhanced the density of dangling bonds of each material of OF, effects of compressive stress on pull-out resistance and elasticity enhancements of fiber and sheath probably occurred. Thus, 0.64 MGy-HLEBI enhanced the (dσ/dε)i and (dσ/dε)max as well as εf, resulting in enhancement of σf of OF.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.