Abstract
The tensile fracture was originated from the strain concentration in equiaxed grain region adjacent to the fusion center, where a lower micro-hardness occurred when compared to the columnar grain region in the fusion zone. A higher stress level was more potential to fabricate a fatal fatigue crack initiating from the intrinsic metallic deficiencies. At a lower stress of 180 MPa, fatigue crack appeared to initiate from the intergranular welding pores other than the intrinsic metallic deficiencies. Furthermore, intergranular welding pores induced fatal crack initiation became the major fatigue crack initiation mechanisms when the fatigue stress amplitude down to 140 MPa.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.