Abstract
Monodispersed Ce3+-doped Y3Al5O12 (YAG:Ce3+) nanospheres were synthesized through forced hydrolysis using a urea method, followed by thermal calcination processes, and their luminescence properties were examined. The crystallization of the YAG:Ce3+ phase and morphological evolutions after subsequent heat treatment were characterized by X-ray powder diffraction (XRD), field-emission scanning electron microscopy (FESEM), and transmission electron microscopy (TEM). Energy dispersive spectroscopy (EDS) analysis revealed that the amorphous aluminum oxide layer played an important role in preventing necking between the particles during heat treatment. As a result, stand-alone YAG:Ce3+ nanospheres with an amorphous aluminum oxide layer shell were synthesized while maintaining monodispersity with an average particle diameter of about 33 nm. These nanospheres had a dense structure and smooth surface with relatively good crystallinity after annealing at 1075 °C. They absorbed light efficiently in the visible region of 400–500 nm, and showed a single broadband emission peak at 536 nm with a luminescence quantum efficiency (QE) of 33% and relatively good photostability.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.