Abstract
The growth of carbon nanotubes(CNTs) in anodic aluminum oxide(AAO) template and their application to a field emitter are described. AAO templates were fabricated by anodizing bulk aluminum and sputtered thin Al film on Nb‐coated Si wafers. After Co catalyst had been electrochemically deposited into the bottom of the pores in AAO template, CNTs were grown by pyrolyzing C2H2. Depending on the reaction conditions, CNTs grew up to or over the top of the pores in AAO template with different structures. The morphology and structure of CNTs were observed with a scanning electron microscope and a transmission electron microscope. The diameter of CNTs strongly depended on the size of the pores in AAO template and the growing conditions. The electron field emission measurement of the samples resulted in the turn‐on field of 1.9–2.2 V/μm and the field enhancement factor of 2450–5200. The observation of high field enhancement factors is explained in terms of low field screening effect.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.