Abstract
Tempering behavior of a 0.53%C-1.6%Si-0.9%Mn-0.76%Cr-0.14%V-0.05%Nb steel was examined. Water quenching produced lath martensite structure with a 10.5% volume fraction of retained austenite (RA) with film-like shape. Low temperature tempering (LTT) leads to precipitation of transition carbides and carbon partitioning between martensite and RA. The following precipitation sequence was found: martensite →non-stoichiometric η-carbide→stoichiometric η-carbide→Fe3C. Highest density of non-stoichiometric Fe2C η−carbides was found after isochronal tempering at 280 °C that provided attractive combination of high yield stress (YS) (1890 MPa) with a ductility of ∼6% and a Charpy V-notch (CVN) impact energy of ∼10 J/cm2. At 400 °C, the replacement of non-stoichiometric η-carbide by the stoichiometric one decreases strength and increases ductility due to 30% decrease in its volume fraction. No tempered martensite embrittlement was found due to the fact that Si effectively suppresses the precipitation of cementite at T ≤ 400 °C. The replacement of transition η-carbide by boundary cementite after isochronal tempering at 500 °C leads to considerably decrease in YS down to 1360 MPa, while elongation to failure increases up to 9.3%. Effect of decomposition of RA on strength, ductility and fracture toughness is insignificant.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.