Abstract
ABSTRACTThe surface-front oxidation mechanism of iron was investigated by time-resolved, glancingangle Fe K-edge fluorescence EXAFS measurements at various oxidation temperatures of 200-700 C. The glancing angle was chosen according to the depth of the oxide layer, roughly 1500-2000A. The oxidation behavior under rapid heating(up to 600°C within 10 minutes) was compared with the slowly heated oxidation process using the Quick-EXAFS measurements. In the slowly heated process, Fe3O4 was the dominating phase at a relatively low temperature (300-400 C) initially. However, at a relatively high temperature (above 600°C), the Fe2O3 and FeO crystalline phases are gradually enriched as the successive oxidation process involving intrusive oxygen proceeded. Remarkably under a prolonged heat treatment above 600°C, the stable FeO phase that exists in a deep-lying interface structure and Fe2O3 phase eventually dominates the thick front-surface structure. In a quickly heated process, however, Fe3O4 phase is less dominating, which is contradictory to the commonly accepted oxidation models. The EXAFS results are discussed in conjunction with the x-ray diffraction features under the same heat treatment conditions.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.