Abstract
Temperature-dependent domains back-switching behavior and nonlinear dielectric response were studied in 200 nm fresh and aged PbZr0.4Ti0.6O3 thin films to compare domain walls motion under large and small signals. Expected thermally activation of domains back-switching and dielectric nonlinearity were observed at low temperature, however, abnormal thermally inhibited behavior occurred at higher temperatures. Such phenomenon was found in both fresh and aged films and the ageing process magnified such thermally inhibited effect. Analyzing nonlinear dielectric response with Rayleigh law suggested that the interaction between domain walls and pinning centers was strengthened at high temperature especially after ageing. Promoted pinning effect by rising temperature could reduce dielectric loss and this is practical for high temperature applications of ferroelectrics.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.