Temperature-dependent dielectric properties and line profile analysis of zinc-substituted copper ferrites

Abstract

Temperature dependence of dielectric constant and loss has been investigated for different compositions of Zinc substituted copper ferrites with general formula Cu1–xZnxFe2O4 (x = 0.0, 0.2, 0.4, 0.6, 0.8, 1.0) prepared by ceramic method. XRD analysis confirms all the samples exhibit single phase cubic spinel structure. The dielectric constant and loss of the sample were studied in the temperature ranges from RT to 1000K at different constant frequency. Samples of the composition with x = 0.8 show low dielectric loss up to a measured temperature around 770 °C at higher frequencies as compared to samples of other compositions. A plot of dielectric constant versus temperature shows a transition near the Curie temperature, an attempt is made to explain the possible mechanism for this observation. The dielectric constant increases slowly from 309°C to 770°C with temperature in the beginning and sharply decreases with increase in frequency for all the samples. The variation of tanδ with frequency shows cusps fo...