Abstract
AbstractSingle phase delafossite p-type CuFeO2 (CFO) semiconductor was synthesized in bulk by modified solid state reaction technique. X-ray diffraction (XRD) and X-ray photo spectroscopy (XPS) studies suggest single phase CFO at room temperature. The energy dispersive X-ray spectroscopy (EDX) revealed that the atomic ratio of Cu and Fe is 1:1. The XPS spectra showed two intense Cu 2p3/2 and 2p1/2 peaks at 932.5 eV and 952 eV suggesting Cu is in +1 state. The temperature dependent Raman spectra of CFO displayed two intense modes at 349 cm-1 and 690 cm-1 at room temperature that matched with other delaffosite structures. The temperature dependent Raman spectra showed significant shift in both Raman active modes to lower frequency side. We observed the disappearance of pure CFO Raman active modes above 750 K and the appearance of new peaks related to CuO compounds, indicating disintegration of CFO starting above 750 K which almost completed above 1100 K. The temperature dependent thermo-gravimetric analysis indicates change in CFO mass above 750 K with wide range of differential thermo-gravimetric slope suggests disintegration started above 750 K and completed at 1100 K. Raman spectra, XPS, and XRD of disintegrated CFO matched well with the Raman spectra, XPS and XRD of CuO and CuFe2O4 confirmed its disintegration above 750 K in air.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call