Abstract
The role of nanoscale heterogeneity on the mode I fracture toughness, KIc, of model epoxy networks has been investigated. Model systems utilized consist of diglycidyl ether of bisphenol A (DGEBA) as the epoxide with a stoichiometric amine mixture of a rigid cycloaliphatic diamine (PACM) and a more flexible, polypropylene glycol based diamine (Jeffamine) at different molar ratios. The molecular weight of the Jeffamine was adjusted to further tailor the epoxy properties. Fracture toughness was measured using single edge notched bend samples and hardness was measured by Vickers indentation. Both measurements were performed at temperatures as low as −100 ̊C to above ambient temperatures. Results are interpreted in the context of the Dugdale model of material toughness where the fracture toughness is expressed in terms of a cohesive zone stress (related to the hardness), the elastic modulus (measured directly) and the crack tip opening displacement (obtained from images of the fracture surfaces). High toughness is obtained in heterogeneous networks where a decrease in the cohesive zone stress is offset by sufficiently large increases in the crack tip opening displacement.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.