Abstract
The spall strength of austenitic steel 12Kh18N10T was measured for times of ~10–7 s in the temperature range of 77–580 K. The feature at ~140 K, which was caused by the mutual influence of spallation and austenite transformation into martensite under tension, was revealed in the temperature–time dependence of the spall strength. A decrease in the spall strength with an increase in temperature was revealed in the temperature range of 300–580 K, which was interpreted in terms of the kinetic strength concept. The published experimental data on the rupture life at times of ~107 s, which agree with the temperature–time dependence of the spall strength in a microsecond range of loading times, were considered. The equation of state of austenitic steel 18-10 was constructed and used to analyze the temperature history of loading in the compression–unloading–tension during spallation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.