Abstract
AC conductivity of a green porcelain body was investigated using impedance spectroscopy over a temperature range of 100–950°C. The results showed that during the heating, conductivity at 100–200°C increased mainly arising from H+ and OH− ions generated from adsorbing physical water. The activation energy increased below the dehydroxylation of clay resulting from movement of monovalent ions. At the dehydroxylation of clay, a combination of H+, OH− and monovalent ions dominated the conductivity. The activation energy rose to 1.14eV (600–950°C) controlled by diffusion of Na+, and K+ ions. During the cooling, conductivity showed single activation energy with 0.86eV resulting from denser microstructure and change in mineralogical constituents and the heat treated porcelain sample showed higher electrical conductivity at the same temperature. Understanding conduction behaviour of the green porcelain enabled more accurate control of furnace temperature in flash sintering, a process which relies on electrical conductivity at high temperatures.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.